LLDPE 1018 Series
ExxonMobil / Premium Origin Original
LLDPE 1018 Series is a premium-grade linear low density polyethylene resin highly celebrated for its extraordinary film mechanical integrity and unparalleled elasticity. Engineered primarily for cast film extrusion and high-performance blown film laminations, this grade boasts a phenomenal transverse elongation at break of 870% combined with a robust tensile breakdown resistance of 50 MPa longitudinally. With its elevated puncture energy rating of 2.9 J and exceptional biaxial tearing equilibrium, it is the premier industry standard for high-speed automatic pallet wrapping stretch films, industrial liners, heavy-duty shipping bags, and multi-layer agricultural laminates.
Request Latest Quote (FOB/CIF):
Inquiry NowTechnical Data Sheet (TDS)
| Property | Typical Value | Test Method |
|---|---|---|
| Tensile Strength at Yield (MD) | 9.6 MPa (1400 psi) | ASTM D882 |
| Tensile Strength at Yield (TD) | 10 MPa (1400 psi) | ASTM D882 |
| Tensile Strength at Break (MD) | 50 MPa (7300 psi) | ASTM D882 |
| Tensile Strength at Break (TD) | 36 MPa (5200 psi) | ASTM D882 |
| Elongation at Break (MD) | 570 % | ASTM D882 |
| Elongation at Break (TD) | 870 % | ASTM D882 |
| Secant Modulus (1% Secant - MD) | 190 MPa (28000 psi) | ASTM D882 |
| Secant Modulus (1% Secant - TD) | 230 MPa (33000 psi) | ASTM D882 |
| Dart Drop Impact Strength | 90 g | ASTM D1709A |
| Elmendorf Tear Strength (MD) | 90 g | ASTM D1922 |
| Elmendorf Tear Strength (TD) | 450 g | ASTM D1922 |
| Puncture Force Resistance | 40 N (9 lbf) | ExxonMobil Method |
| Puncture Energy Absorption | 2.9 J (25 in·lb) | ExxonMobil Method |