HDPE 50100
HDPE 50100 is an elite-tier, high-molecular-weight, bimodal high-density polyethylene resin engineered specifically for heavy-duty extrusion blow molding and structural sheet co-extrusion architectures. Characterized by a robust fractional high-load melt flow rate (HLMFR) of 10.0 g/10 min and exceptional melt strength, this grade delivers outstanding parison stability and zero sag control during automated mass-scale molding. Demonstrating a masterfully balanced 1207 MPa flexural modulus combined with an extraordinary environmental stress-crack resistance (ESCR) threshold exceeding 600 hours, it provides supreme hydraulic impact cushioning and lifetime defensive armor against harsh industrial chemicals, making it the definitive global benchmark for large-scale Jerry cans, agricultural chemical containers, hazardous material fuel tanks, and massive 200L shipping drums.
Request Latest Quote (FOB/CIF):
Inquiry NowTechnical Data Sheet (TDS)
| Property | Typical Value | Test Method |
|---|---|---|
| Physical: High Load Melt Flow Rate (190°C / 21.60 kg HLMFR) | 10.0 g/10min | ASTM D1238 |
| Physical: Density (23°C) | 0.950 g/cm³ | ASTM D1505 |
| Physical: Antioxidant Package | Yes | — |
| Mechanical: Tensile Strength at Yield (50.8 mm/min) | 25 MPa | ASTM D638 |
| Mechanical: Tensile Elongation at Break (50.8 mm/min) | 700 % | ASTM D638 |
| Mechanical: Flexural Modulus (Initial Tangent) | 1207 MPa | ASTM D790A |
| Mechanical: Tensile Impact Strength (Type S bar) | 189 kJ/m² | ASTM D1822 |
| Mechanical: Shore Hardness (Shore D Durometer) | 68.0 | ASTM D2240 |
| Thermal: Vicat Softening Temperature (VST 10 N) | 126 °C | ASTM D1525 |
| Thermal: Heat Deflection Temperature (HDT 0.455 MPa) | 78 °C | ASTM D648 |
| Reliability: Environmental Stress Crack Resistance (ESCR, Cond. B, 100% Igepal, F50) | >600 hr | ASTM D1693 |